美國陶氏-LLDPEHMS8017-不含開口劑和增滑劑-薄膜吹塑專用
價格
訂貨量(千克)
¥7.98
≥25
¥7.90
≥1000
店鋪主推品 熱銷潛力款
莸莾莺莶莶莼莺莾莼莶莵
在線客服
性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
物理性能 | 比重 | ASTMD792 | 0.918 | g/cm3 | |
熔流率(熔體流動速率)(190°C/2.16kg) | ASTMD1238 | 0.75 | g/10min | ||
薄膜 | 薄膜厚度-經測試 | 51 | μm | ||
割線模量 | 2%正割,MD:51μm | ASTMD882 | 168 | MPa | |
2%正割,TD:51μm | ASTMD882 | 176 | MPa | ||
抗張強度 | MD:屈服,51μm | ASTMD882 | 10.4 | MPa | |
TD:屈服,51μm | ASTMD882 | 10.6 | MPa | ||
MD:斷裂,51μm | ASTMD882 | 49.2 | MPa | ||
TD:斷裂,51μm | ASTMD882 | 43.2 | MPa | ||
伸長率 | MD:斷裂,51μm | ASTMD882 | 630 | % | |
TD:斷裂,51μm | ASTMD882 | 730 | % | ||
落錘沖擊(51μm) | ASTMD1709A | 420 | g | ||
埃爾曼多夫抗撕強度 | MD:51μm | ASTMD1922 | 790 | g | |
TD:51μm | ASTMD1922 | 1100 | g | ||
薄膜厚度-經測試 | 51 | μm | |||
割線模量 | 2%正割,MD:51μm | ASTMD882 | 168 | MPa | |
2%正割,TD:51μm | ASTMD882 | 176 | MPa | ||
抗張強度 | MD:屈服,51μm | ASTMD882 | 10.4 | MPa | |
TD:屈服,51μm | ASTMD882 | 10.6 | MPa | ||
MD:斷裂,51μm | ASTMD882 | 49.2 | MPa | ||
TD:斷裂,51μm | ASTMD882 | 43.2 | MPa | ||
伸長率 | MD:斷裂,51μm | ASTMD882 | 630 | % | |
TD:斷裂,51μm | ASTMD882 | 730 | % | ||
落錘沖擊(51μm) | ASTMD1709A | 420 | g | ||
埃爾曼多夫抗撕強度 | MD:51μm | ASTMD1922 | 790 | g | |
TD:51μm | ASTMD1922 | 1100 | g | ||
熱性能 | 熔融溫度 | DSC | 121 | °C | |
光學性能 | 光澤度(45°,51.0μm) | ASTMD2457 | 82 | ||
霧度(51.0μm) | ASTMD1003 | 8.4 | % |