美國陶氏-LLDPEHS-7021NT7-高光澤抗撕裂-流延膜專用料
價格
訂貨量(千克)
¥7.98
≥25
¥7.90
≥1000
店鋪主推品 熱銷潛力款
憩憭憫憦憦憪憫憭憪憦憧
在線客服
性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
基本性能 | 比重 | ASTM D-792 | 0.919 | g/cm3 | |
熔體流動速率 | 190℃/2.16kg | ASTM D-1238 | 3.2 | g/10min | |
機械性能 | 電影穿刺能源 | 20.3um | Internal Method | 3.16 | J |
50.8um | Internal Method | 7.91 | J | ||
電影穿刺力 | 20.3um | Internal Method | 35.6 | N | |
50.8um | Internal Method | 84.5 | N | ||
電影穿刺抵抗 | 20.3um | Internal Method | 22.5 | J/cm3 | |
50.8um | Internal Method | 21.8 | J/cm3 | ||
電影韌性(MD) | 20.3um | ASTM D-882 | 320 | J/cm3 | |
電影韌性(TD) | 20.3um | ASTM D-882 | 276 | J/cm3 | |
電影韌性(MD) | 50.8um | ASTM D-882 | 246 | J/cm3 | |
電影韌性(TD) | 50.8um | ASTM D-882 | 287 | J/cm3 | |
割線模量-2% Secant(MD) | 20.3um | ASTM D-882 | 149 | MPa | |
割線模量-2% Secant(TD) | 20.3um | ASTM D-882 | 158 | MPa | |
割線模量-2% Secant(MD) | 50.8um | ASTM D-882 | 156 | MPa | |
割線模量-2% Secant(TD) | 50.8um | ASTM D-882 | 155 | MPa | |
拉伸屈服強度(MD) | 20.3um | ASTM D-882 | 12.3 | MPa | |
拉伸屈服強度(TD) | 20.3um | ASTM D-882 | 11.2 | MPa | |
拉伸屈服強度(MD) | 50.8um | ASTM D-882 | 10.5 | MPa | |
拉伸屈服強度(TD) | 50.8um | ASTM D-882 | 14.8 | MPa | |
拉伸斷裂強度(MD) | 20.3um | ASTM D-882 | 60.2 | MPa | |
拉伸斷裂強度(TD) | 20.3um | ASTM D-882 | 40.8 | MPa | |
拉伸斷裂強度(MD) | 50.8um | ASTM D-882 | 40.6 | MPa | |
拉伸斷裂強度(TD) | 50.8um | ASTM D-882 | 56.3 | MPa | |
拉伸斷裂伸長率(MD) | 20.3um | ASTM D-882 | 580 | % | |
拉伸斷裂伸長率(TD) | 20.3um | ASTM D-882 | 880 | % | |
拉伸斷裂伸長率(MD) | 50.8um | ASTM D-882 | 730 | % | |
拉伸斷裂伸長率(TD) | 50.8um | ASTM D-882 | 610 | % | |
落錘沖擊(MD) | 20.3um | ASTM D-1709A | 96 | g | |
落錘沖擊(TD) | 20.3um | ASTM D-1709B | <100 | g | |
落錘沖擊(MD) | 50.8um | ASTM D-1709A | 330 | g | |
落錘沖擊(TD) | 50.8um | ASTM D-1709B | 130 | g | |
埃爾曼多夫撕裂強度(MD) | 20.3um | ASTM D-1922 | 160 | g | |
埃爾曼多夫撕裂強度(TD) | 20.3um | ASTM D-1922 | 570 | g | |
埃爾曼多夫撕裂強度(MD) | 50.8um | ASTM D-1922 | 760 | g | |
埃爾曼多夫撕裂強度(TD) | 50.8um | ASTM D-1922 | 980 | g | |
斷裂拉伸(MD) | 0.0203mm | Internal Method | 360 | % | |
斷裂拉伸(TD) | 0.0508mm | Internal Method | 570 | % | |
加工性能 | 熔體溫度 | 271 | ℃ | ||
熱性能 | 維卡軟化點 | ASTM D-1525 | 100 | ℃ | |
熔化溫度 | Internal Method | 123 | ℃ | ||
光學性能 | 光澤度 | 20°,20.3um | ASTM D-2457 | 157 | |
20°,50.8um | ASTM D-2457 | 143 | |||
45°,20.3um | ASTM D-2457 | 95 | |||
45°,50.8um | ASTM D-2457 | 90 | |||
霧度 | 20.3um | ASTM D-1003 | 1 | % | |
50.8um | ASTM D-1003 | 4 | % |