美國陶氏-LLDPEHS-7028NT7-抗開裂高韌性強度-用于管材和薄膜
價格
訂貨量(千克)
¥7.98
≥25
¥7.90
≥1000
店鋪主推品 熱銷潛力款
専將将專專尊将將尊專尋
在線客服
性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
基本性能 | 比重 | ASTM D-792 | 0.918 | g/cm3 | |
熔體流動速率 | 190℃/2.16kg | ASTM D-1238 | 1 | g/10min | |
機械性能 | 電影穿刺能源 | 20.3um | Internal Method | 3.39 | J |
50.8um | Internal Method | 5.08 | J | ||
電影穿刺力 | 20.3um | Internal Method | 40 | N | |
50.8um | Internal Method | 71.2 | N | ||
電影穿刺抵抗 | 20.3um | Internal Method | 20.9 | J/cm3 | |
50.8um | Internal Method | 13 | J/cm3 | ||
電影韌性(MD) | 20.3um | ASTM D-882 | 295 | J/cm3 | |
電影韌性(TD) | 20.3um | ASTM D-882 | 341 | J/cm3 | |
電影韌性(MD) | 50.8um | ASTM D-882 | 253 | J/cm3 | |
電影韌性(TD) | 50.8um | ASTM D-882 | 289 | J/cm3 | |
割線模量-2% Secant(MD) | 20.3um | ASTM D-882 | 204 | MPa | |
割線模量-2% Secant(TD) | 20.3um | ASTM D-882 | 233 | MPa | |
割線模量-2% Secant(MD) | 50.8um | ASTM D-882 | 199 | MPa | |
割線模量-2% Secant(TD) | 50.8um | ASTM D-882 | 183 | MPa | |
拉伸屈服強度(MD) | 20.3um | ASTM D-882 | 16 | MPa | |
拉伸屈服強度(TD) | 20.3um | ASTM D-882 | 15.4 | MPa | |
拉伸屈服強度(MD) | 50.8um | ASTM D-882 | 12.2 | MPa | |
拉伸屈服強度(TD) | 50.8um | ASTM D-882 | 11 | MPa | |
拉伸斷裂強度(MD) | 20.3um | ASTM D-882 | 60.7 | MPa | |
拉伸斷裂強度(TD) | 20.3um | ASTM D-882 | 48.2 | MPa | |
拉伸斷裂強度(MD) | 50.8um | ASTM D-882 | 40.8 | MPa | |
拉伸斷裂強度(TD) | 50.8um | ASTM D-882 | 46.9 | MPa | |
拉伸斷裂伸長率(MD) | 20.3um | ASTM D-882 | 580 | % | |
拉伸斷裂伸長率(TD) | 20.3um | ASTM D-882 | 800 | % | |
拉伸斷裂伸長率(MD) | 50.8um | ASTM D-882 | 700 | % | |
拉伸斷裂伸長率(TD) | 50.8um | ASTM D-882 | 850 | % | |
落錘沖擊(MD) | 20.3um | ASTM D-1709A | 94 | g | |
落錘沖擊(TD) | 20.3um | ASTM D-1709B | <100 | g | |
落錘沖擊(MD) | 50.8um | ASTM D-1709A | 130 | g | |
落錘沖擊(TD) | 50.8um | ASTM D-1709B | 270 | g | |
埃爾曼多夫撕裂強度(MD) | 20.3um | ASTM D-1922 | 300 | g | |
埃爾曼多夫撕裂強度(TD) | 20.3um | ASTM D-1922 | 670 | g | |
埃爾曼多夫撕裂強度(MD) | 50.8um | ASTM D-1922 | 820 | g | |
埃爾曼多夫撕裂強度(TD) | 50.8um | ASTM D-1922 | 1200 | g | |
密封起始溫度 | 20.3um | Internal Method | 110 | ℃ | |
50.8um | Internal Method | 120 | ℃ | ||
密封強度 | 150℃,0.0203mm | Internal Method | 1000 | g | |
150℃,0.0508mm | Internal Method | 2100 | g | ||
熱性能 | 維卡軟化點 | ASTM D-1525 | 103 | ℃ | |
熔化溫度 | Internal Method | 124 | ℃ | ||
光學性能 | 光澤度 | 20°,20.3um | ASTM D-2457 | 62 | |
20°,50.8um | ASTM D-2457 | 90 | |||
45°,20.3um | ASTM D-2457 | 50 | |||
45°,50.8um | ASTM D-2457 | 61 | |||
霧度 | 20.3um | ASTM D-1003 | 12 | % | |
50.8um | ASTM D-1003 | 18 | % |